تفاصيل المنتج:
اتصل
نتحدث الآن
|
| اسم المنتج: | راتنج الايبوكسي الجص | مادة: | راتنج الايبوكسي |
|---|---|---|---|
| مظهر: | سائل | الاستخدام: | الحشو ، والتوصيل ، مقاوم للماء |
| حزمة النقل: | برميل 10L | قوة ضاغطة: | ≥70 |
| حياة الصلاحية: | ≥15 | قوة الرابطة الجافة: | ≥4.0 |
| قوة الترابط الرطب: | ≥3.0 | ||
| إبراز: | Modified Epoxy Resin Grout,Two Component Epoxy Resin Grout,High Permeability Polyurethane Grouting,Two Component Epoxy Resin Grout,High Permeability Polyurethane Grouting |
||
This high-performance epoxy resin injection grout is a two-component, low-viscosity formulation designed for concrete repair and structural reinforcement applications. The product cures at low temperatures and can harden even in water, with controllable curing time and non-shrinkage characteristics after curing.
Specifically engineered for concrete structure crack leakage repair, this epoxy grout demonstrates excellent binding force with various structural materials. When applied using mechanical high-pressure injection, it effectively seals micro-cracks while providing structural reinforcement.
Ideal for filling and reinforcing construction joints, deformation joints, cracks, and hollows in various concrete structures including bridges, subways, tunnels, channels, water conservancy dams, mine rock formations, and harbor projects.
During transport, protect from rain and direct sunlight. Handle carefully to avoid collisions and falls. Store in sealed containers in dry, ventilated areas away from direct sunlight and rain, with storage temperature not exceeding 40°C.
| Test Item | Unit | Index |
|---|---|---|
| Density | G/Cm³ | >1.00 |
| Compressive Strength | Mpa | ≥ 70 |
| Tensile Strength | Mpa | ≥ 15 |
| Dry Bond Strength | Mpa | ≥ 4.0 |
| Wet Bonding Strength | Mpa | ≥ 3.0 |
| Impermeability Pressure | Mpa | ≥ 1.2 |
| Anti-seepage Pressure Ratio | % | ≥ 400 |
| Parameter | 1:1 Ratio | 4:1 Ratio |
|---|---|---|
| Product Proportion | Main agent: 10kg, Curing agent: 10kg | Main agent: 20kg, Curing agent: 5kg |
| Mixing Ratio | A:B = 1:1 | A:B = 4:1 |
| Slurry Density (G/Cm³) | 1.16 | 1.16±0.05 |
| Initial Viscosity (Mpa/S) | 190 | 30 minutes (23℃ ±2℃) |
| Initial Hardening | 40 minutes - 2 hours | 10 hours |
| Operational Time | 40 minutes | 40 minutes |
| Compressive Strength | 70 MPA | ≥ 70 MPA |
| Impermeable Pressure | 1.5 | ≥ 1.2 |
Synthetic resin type mixed into a milky yellow liquid, setting at room temperature in approximately 30 minutes.
Fast curing formulation with light yellow appearance, initial setting at room temperature in approximately 30 minutes.
High permeability formulation with light red amber color, initial setting at room temperature in approximately 30 minutes.
Strong Bonding Force Reinforcement Does Not Leak
Jiangsu Lihong Technology Development Co., Ltd. is a national high-tech enterprise integrating R&D, production, sales, and technical services. Located in the Salt Chemical New Materials Industrial Park in Huai'an City, Jiangsu Province, the company covers 150 acres with total investment exceeding RMB 500 million and annual production capacity of over 100,000 tons.